Description
ePLA-GF
The glass fiber reinforced pla filament is developed on the basis of PLA is added with 16% glass fiber, which greatly enhances the rigidity and impact resistance of ordinary PLA. The ePLA-GF’s bending modulus is as high as 4400MPa, which is highly rigid and not easy to distort;
| Filament Properties Table | |
|---|---|
| 3D PRINTING FILAMENT | ePLA-GF |
| Density(g/cm3) | 1.31 |
| Heat Distortion Temp(℃,0.45MPa) | 56 5/10 |
| Melt Flow Index(g/10min) | 6.36（190℃/2.16kg） |
| Tensile Strength(MPa) | 59.27 7/10 |
| Elongation at Break(%) | 7.99 1/10 |
| Flexural Strength(MPa) | 85.01 8/10 |
| Flexural Modulus(MPa) | 4414.89 8/10 |
| IZOD Impact Strength(kJ/㎡) | 10.16 2/10 |
| Durability | 4/10 |
| Printability | 9/10 |
| Recommended printing parameters | |
| Extruder Temperature(℃) | 190 – 230℃ Recommended temperature：215℃ |
| Bed temperature(℃) | 45 – 60°C |
| Fan Speed | 100% |
| Printing Speed | 40 – 100mm/s |
| Heated Bed | Optional |
| Recommended Build Surfaces | Masking paper, PVP solid glue, PEI |
| Feature | |
| Flexible | —— |
| Elastic | —— |
| Impact Resistant | √ |
| Soft | —— |
| Composite | √ |
| UV Resistant | —— |
| Water Resistant | —— |
| Dissolvable | —— |
| Heat Resistant | —— |
| Chemically Resistant | —— |
| Fatigue Resistant | —— |
| Need drying | —— |
| Heated Bed Required | —— |
| Print recommend | —— |
Notes:
1. ePLA-GF line has strong rigidity and is not easy to bend. In the feeding pipeline, excessive bending of filament should be avoided as far as possible
2. ePLA-GF is very easy to grind the nozzle and extruder gear. It is recommended to use hardened steel nozzle or ruby nozzle. If conditions permit, hardened steel extruder gear can be selected. If the printing time is long and the plug occurs, the throat and nozzle need to be replaced
3. The blowing fan can be properly turned off to improve the model strength